High-strength, High-alumina Castable refractory
|
Brands
Items |
LC-160 |
LC-140 |
|
Chemical composition |
Al2O3 |
≥75 |
≥75 |
|
SiO2 |
≤20 |
≤20 |
|
Max appl,
℃ |
1600 |
1300 |
|
Bulk density after burnt at (g/cm3) |
≥2.75 |
≥2.65 |
|
PLC (1500℃×3h),
% |
0.1-0.5 |
0.2-0.4 (800℃×3h) |
|
CCS/MOR, MPa |
110℃×24h |
80/9 |
60/8 |
|
1100℃×3h |
100/15 |
90/8 |
|
1500℃×3h |
150/15 |
- |
|
Max grain size of aggregate, mm |
5-6 |
5-6 |
|
Water needed for installation, % |
6-7 |
6-7 |
|
Application |
Used in the mouth of the middle size and
small size cement kilns, the sides of
cooler, prefabricated crane girder of
tintering device in metallurgical
industry. |
Used in middle size furnaces in the
industries of cement, oil chemical
machinery metall |
Data sheet of zirconia-corundum castables
|
|
AZS50V |
AZS06L |
AZS04J |
|
Al2O3, % |
≥65 |
≥75 |
≥80 |
|
ZrO2, % |
≥29 |
≥30 |
≥30 |
|
SiO2, % |
≤20 |
≤18 |
≤18 |
|
BD, g/cm3 |
≥3.00 |
≥2.65 |
≥2.80 |
|
MOR, MPa |
110℃×24h |
≥11.5 |
|
≥12.1 |
|
1110℃×2h |
≥18 |
|
≥18 |
|
CS, MPa |
110℃×24h |
≥85 |
|
≥85 |
|
1110℃×2h |
≥100 |
|
≥100 |
|
Resistance to glass |
Good |
Good |
Good |
|
Bubbling trend |
|
|
|
|
Water needed for installation, % |
4~5 |
8~10 |
10~11 |
|
Applications |
As seals up layer of furnace bottom, and
above insulating layer |
Use at above the 50V, below the pavement
brick |
For use in joints of pavement bricks. |
Data sheet of zircon ramming mixes
|
|
Zircon ramming mix |
|
ZrO2, % |
≥60 |
|
Refractoriness, ℃ |
≥1790 |
|
BD, g/cm3 |
≥3.50 |
|
service density, kg/m3 |
3600 |
|
CCS, MPa |
110℃×24h, ≥45 |
|
Max application temperature, ℃ |
1650 |
Data sheet of fused AZS ramming mix
|
|
Fused AZS ramming mix |
|
ZrO2, % |
≥28 |
|
Refractoriness, ℃ |
≥1770 |
|
BD, g/cm3 |
≥2.90 |
|
Using Density, kg/m3 |
3000 |
|
CCS, MPa |
110℃×24h, ≥50 |
|
Max application temperature, ℃ |
1650 |
|
|
|
|
|